The result indicated that high drawing temperature and great drawing temperature gradient were the cause of ballrace craze;This was verified on our production.
結(jié)果表明,滾道回火溫度高和回火溫度梯度過大都是導(dǎo)致裂紋產(chǎn)生的原因;并在生產(chǎn)中得到驗(yàn)證。
The cause of the ballrace craze of our product was analyzed by means of fractography,metallographic examination,ingredient analyses,electron microscope analyses and rigidity detection,etc.
采用斷口分析、金相檢驗(yàn)、成份分析、電鏡分析和硬度檢測等方法對(duì)某產(chǎn)品用的滾道分析了產(chǎn)生裂紋的原因。
Keywords ballrace;rupture drawing;temperature;failure anaysis;
滾道;斷裂;回火溫度;失效分析;
The result indicated that high drawing temperature and great drawing temperature gradient were the cause of ballrace craze;
結(jié)果表明,滾道回火溫度高和回火溫度梯度過大都是導(dǎo)致裂紋產(chǎn)生的原因;