crushing strength

基本解釋

The influence of green ball quality and palletizing crushing strength are studied by using different size distribution of DAYE concentrate.
研究了不同的粒度組成大冶鐵精礦對(duì)生球質(zhì)量與成品球團(tuán)抗壓強(qiáng)度的影響。
In addition, according to the crushing strength and physical, chemical properties of manganese nodule, the testing method for crushing using toothed roll crusher is established.
同時(shí)根據(jù)錳結(jié)核的破碎強(qiáng)度和物理化學(xué)特性確定了用齒輥破碎方式進(jìn)行破碎的實(shí)驗(yàn)方法。
The bulk crushing strength and Abrasion strength are evidently different with the category of activated carbon.
測(cè)定了原粒度活性炭的堆積壓碎強(qiáng)度和磨耗強(qiáng)度。

Not only does the robot look Terminator-esque, but it's been designed to mimic the muscle system of a human (with bone-crushing strength, of course) and will be programmed with a semi-autonomous AI so that the android can learn new tasks, all of which is just a little too much like the Terminator for our comfort.
ENGADGET: Prepare to be terminated: The Kibertron

壓碎強(qiáng)度
The porosity(Pa)was 36.97%,water absorption(Wa)was 20.34%,bulk density(D)was 1.82kg/m~3,crushing strength was 13.50MPa,acid resistance was 96.76%and alkali resistance was 97.38%,when the optimal sample YC2 was fired at 1080℃with 20 wt%additional content of graphite added.
典型配方Y(jié)C2石墨添加量達(dá)20wt%(外加),于1080℃下燒成樣品的顯氣孔率為36.97%,吸水率為20.34%,體積密度為1.82kg/m~3,抗壓碎強(qiáng)度為13.50MPa,耐酸性為96.76%,耐堿性為97.38%。
化學(xué)
耐壓強(qiáng)度
By reducing the addition of reused magnesia chrome bricks,the crushing strength,MOR and bulk density became higher after drying and firing at medium and high temperature.
隨著廢鎂鉻磚加入量的降低,烘干、中溫和高溫處理后的耐壓強(qiáng)度、抗折強(qiáng)度、體積密度均逐漸增大。
醫(yī)藥科學(xué)
抗碎強(qiáng)度