CdZnTe

基本解釋

A 60mm diameter CdZnTe(CZT) ingot with the single-crystal volume over 200cm~3 was successfully grown by using seeded modified vertical Bridgman(MVB) method.
采用改進(jìn)的垂直布里奇曼(MVB)法并引入籽晶生長技術(shù),成功生長出直徑60mm,單晶體積超過200 cm3的CdZeTe(CZT)晶錠。
Utilize the angle relation among faces of CdZnTe crystals and use the laser positive reflect method to orientate the CdZnTe single crystals grown by improved Bridgman method, thereby, (111)and(100) faces of CdZnTe crystal were grinded.
利用CdZnTe晶體晶面夾角之間的關(guān)系采用激光正反射法對改進(jìn)布里奇曼法生長的CdZnTe單晶進(jìn)行定向,研磨出了CdZnTe單晶體的(111)、(100)面。
The asymmetrical Bragg reflection STD scan mode with the conventional X-ray diffraction rocking curve was used to determine the lattice distortion of CdZnTe single crystal in this method.
在高分辨X射線衍射儀上,利用不對稱布拉格衍射STD技術(shù)與單晶搖擺曲線技術(shù)相結(jié)合的方法,對碲鋅鎘單晶材料的晶格畸變進(jìn)行了分析測定。
Keywords CdZnTe;ACRT-VBM;crystal growth system;
坩堝加速旋轉(zhuǎn)-垂直下降法;晶體生長設(shè)備;
Discriminator grade CdZnTe detector
甄別級CdZnTe探測器