oblique crack
基本解釋
- [交通運輸工程]斜裂紋
- [物理學(xué)]斜裂紋
英漢例句
- A static, semi-infinite plane problem with an internal oblique crack, in which surfaces are subject to continuous distributed forces, was discussed.
靜態(tài),半無限平面問題的內(nèi)部斜裂紋,表面是連續(xù)分布的力量,進行了討論。 - The macro profile and physicochemical examination of the tread oblique crack shows that the crack falls into the category of rolling contact fatigue type.
踏面斜裂紋及斷口的宏觀形貌和理化檢驗與分析表明,踏面斜裂紋傷損屬于滾動接觸疲勞裂紋傷損類型。 - A study of crack prevention under tensile load is performed on an aluminum alloy 2A12 specimen with an oblique spatial crack by using electromagnetic heating online.
選擇帶有空間斜裂紋的2A12鋁合金試件進行了拉伸載荷作用下電磁熱在線止裂研究。
hkxb.buaa.edu.cn
雙語例句
詞組短語
- oblique angle crack 斜角裂縫
- unilateral oblique crack 單邊斜裂紋
- ellipse oblique crack 橢圓形斜裂紋
- oblique crack on web plate 腹板斜裂縫
- Oblique crack of rail tread 鋼軌踏面斜裂紋
短語
專業(yè)釋義
- 斜裂紋
As a type of rail defects, rail tread oblique crack has been paid extensively attentions in recent years. It will cause rail transversal failure and endanger the traveling safety if it severely develops.
鋼軌踏面斜裂紋屬于鋼軌疲勞傷損,是近年來反映突出的鋼軌傷損類型之一,發(fā)展嚴(yán)重時將導(dǎo)致鋼軌的橫向斷裂而危及行車安全,國外及國內(nèi)已發(fā)生多起由踏面斜裂紋導(dǎo)致鋼軌橫向斷裂的事故。物理學(xué)
- 斜裂紋
The finite element software ANSYS was expanded to compute SIF, computing the SIF of unilateral oblique crack, central crack, central oblique crack, cracks at hole.
4.?dāng)U展了有限元軟件ANSYS計算斷裂參量應(yīng)力強度因子的功能,具體計算了單邊斜裂紋、中心裂紋、中心斜裂紋、孔邊裂紋的應(yīng)力強度因子。