slow strain rate test

基本解釋

Stress corrosion cracking of an X60 pipeline steel in soil containing water has been investigated using slow strain rate test.
用光滑試樣慢應(yīng)變速率拉伸法研究了X60管線鋼在含水土壤中的應(yīng)力腐蝕。
On the base of above appoints, the slow strain rate test was used to study the effect of prestraining on the SCC susceptibility of X70 pipeline steel in simulate soil media.
基于以上的觀點(diǎn)，本文采用慢應(yīng)變速率實(shí)驗(yàn)方法探討了預(yù)形變對X70管線鋼在模擬土壤介質(zhì)中應(yīng)力腐蝕敏感性的影響。
Stress corrosion crack (SCC) susceptibility of titanium alloy TA7 in methanol and hydrochloric acid-methanol solutions was studied by slow strain rate tensile test (SSRT), SEM and optical photography.
采用慢應(yīng)變速率試驗(yàn)，輔以掃描電鏡、金相觀察等分析測試技術(shù)，研究了鈦合金TA7在甲醇、鹽酸-甲醇溶液中的應(yīng)力腐蝕敏感性。