stress induced corrosion

常見(jiàn)例句

High environment humidity increases the susceptibility to hydrogen induced cracking and stress corrosion cracking.
高濕度能增大氫致裂紋和應(yīng)力腐蝕開(kāi)裂傾向。
The result indicated that the failure cause of the stainless steel spiral pipe is the stress corrosion crack induced by Cl- ion.
結(jié)果表明，不銹鋼盤(pán)管失效的原因是氯離子引起的應(yīng)力腐蝕開(kāi)裂所致。
The sulfide induced stress corrosion cracking(SSCC) behavior of the weld seam and base metal of pipeline steel X80 was investigated by using the 3-point bend loading method in H2S environment.
采用三點(diǎn)彎曲加載法，研究了國(guó)產(chǎn)X80管線鋼及其焊接接頭的抗H2S環(huán)境應(yīng)力腐蝕開(kāi)裂（SSCC）行為。