基本解釋

In order to eliminate the defects caused by transverse corner crack of bloom, the morphology and microstructure and principle of crack formation was researched.
為消除由于連鑄坯角部橫裂而產(chǎn)生的缺陷，通過對連鑄包晶鋼裂紋形貌、組織和裂紋形成機(jī)理的研究。
rjggy.net
This article analyzes the mechanism of development and affecting factors of transverse corner crack in slab and puts forward the relative measures which have improved slab quality so much.
對板坯三角區(qū)裂紋的形成機(jī)理及影響因素進(jìn)行分析，并提出相應(yīng)的解決辦法，改善了鑄坯質(zhì)量。
Transverse corner crack is one of the most serious problems in continuous cast slab. With a great number of cracks the slab will witness serious defects and practical operation is badly influenced.
角部橫向裂紋（簡稱角部橫裂）是連鑄板坯較嚴(yán)重的表面缺陷之一，其對鑄坯的生產(chǎn)和質(zhì)量影響很大。