water quenching

基本解釋

• 水淬火

英漢例句

雙語例句

• The circumstance of service was simulated by water quenching and the thermal stress was analyzed.
  利用水淬法模擬其服役狀況并用有限差分方法對產生的非穩(wěn)態(tài)熱應力進行了分析。
• Experiments for hot mold shell with isolated hot spot by local water quenching in investment casting before and after pouring were conducted.
  對熔模鑄件孤立熱節(jié)熱型殼進行了澆注前及澆注后局部水淬激冷試驗。
• However, brine or water quenching is capable of rapidly bringing the surface of the quenched part to its own temperature and maintaining it at or close to this temperature.
  然而鹽水或水淬火能夠將被淬零件的表面迅速冷卻至本身溫度并將其保持或接近此溫度。

• water quenching更多例句

詞組短語

短語

• water soluble quenching liquid 水溶性淬火劑
• water base quenching 水基淬火液
• low water coke quenching 低水熄焦
• water -quenching steel 水淬鋼
• low water coke quenching process 低水熄焦工藝

• water quenching更多詞組

專業(yè)釋義

能源科學技術

• 水淬

  Fine lath martensite can be obtained in the core part of the steel with diameters of 26 mm under 880℃(20℃water quenching)and 940℃(37℃water quenching).
  淬火加熱溫度880℃(20℃水淬)及940℃(37℃水淬)熱處理條件下,直徑為26 mm的試驗鋼心部可獲得細小的板條馬氏體。

• 水冷

  Compared with 00Ni14Cr3Mo3Ti maraging steel, the Cr content of 00Ni13Cr9MoTi maraging steel increases from 3.19% to 8.92% so as to reduce Ms point to 60℃. So water quenching is needed before cold treatment 2h at -73℃.
  和00Ni14Cr3Mo3Ti馬氏體時效鋼相比,00Ni13Cr9MoTi馬氏體時效鋼的Cr含量從3.19%增加到8.92%,使得Ms降到60℃,所以在770-1050℃固溶處理后水冷,并在-73℃冷處理2h,使γ→α轉變時奧氏體盡可能多的轉變成馬氏體,以保證鋼有足夠高的強度。

  機械工程

• 水淬火