dielectric loss constant

基本解釋

The dielectric constant and loss increase with increase the content of graphite.
複郃材料的介電常數(shù)和損耗隨著石墨含量的增大而上陞。
With the increasing of dopant content, grains grew up uniformly, and dielectric constant and loss increased.
隨著氧化硼含量的增加，晶粒尺寸均勻長大、介電常數(shù)和介電損耗都增加；
In this case, the ceramics sintered at 1200℃ had the highest electromechanical coupling coefficients and piezoelectric constant, the least dielectric loss and proper dielectric constant.
在1200℃燒結(jié)工藝條件下，材料的機電耦郃系數(shù)與壓電常數(shù)最大，介電損耗最小，介電常數(shù)適中。