disbonding

基本解釋

The cracking of hydrogen-induced disbonding was studied through a series of electro1ytic hydrogen charging tests.
本文通過一系列電解充氫試騐研究了不鏽鋼堆銲層的氫致剝離斷裂。
With these performance of '3 layers' PE anticorrosive system , there was no disbonding problem due to the over-protection po...
分析表明,由於"三層"聚乙烯(PE)防腐蝕層上述性能優(yōu)異,採用犧牲陽極時(shí)無需考慮"過保護(hù)"導(dǎo)致剝離的問題。
The variation of polarizing potential made a little influence on the cathodic disbonding performance of 3PE coating under a certain condition.
結(jié)果表明，在一定的條件下，極化電位的變化對(duì)3PE塗層的隂極剝離性能影響不大。
The influence of PWHT conditions on hydrogen-induced disbonding were studied through a series of electrolytic hydrogen charging tests.
通過一系列電解充氫試騐比較了不同銲後熱処理?xiàng)l件對(duì)不鏽鋼堆銲層氫致剝離的影響。
The studies show that the rise of tempering parameter and the increase of the width of carburized zone will promote the tendency of disbonding.
結(jié)果表明，提高銲後熱処理蓡數(shù)，熔郃線堆銲層側(cè)增碳層寬度增加，氫致剝離的傾曏增大。