softening temperature

基本解釋

The effect of high silicon low iron material on softening temperature, balling index, quality and output of sintering ore was investigated.
分析了高矽低鉄物料對鉛鋅鑛軟化溫度、成球性指數(shù)、燒結(jié)鑛質(zhì)量與産量的影響。
Cryogenic grinding has been the development trend for ultrafine grinding of plastics, especially for plastics with low softening temperature.
低溫粉碎是塑料，特別是低軟化溫度塑料超細粉碎的發(fā)展趨勢。
The best peak firing temperature was existed, which was between the softening temperature and the peak crystallization temperature, and near the incipient crystallization temperature of the glass.
電阻漿料存在最佳峰值燒成溫度。理論分析表明，最佳峰值燒成溫度應在軟化點與峰值析晶溫度之間，靠近起始析晶溫度。

軟化溫度
The high temperature performance of Ti2AlN was investigated by high temperature microscope. The softening temperature of Ti2AlN was at the range of 1500℃—1580℃and its melting temperature was higher than 1700℃.
高溫顯微鏡研究了單相Ti2AlN的高溫行爲，1500℃—1580℃溫度範圍是Ti2AlN材料的軟化溫度，其熔融溫度大於1700℃。
化學
軟化溫度
Glass fiber modified by Silane coupling agent had the mechanical properties and Vicat softening temperature better than that of the non-modified glass fiber.
其中經(jīng)矽烷偶聯(lián)劑改性過的玻璃纖維力學性能和維卡軟化溫度都會好於未改性的玻璃纖維。
軟化點