hard-segment

常見(jiàn)例句

• Nano-montmorillonite-aliphatic PU elastomer synthesized from HMDI, PTMG1000 and MMT2 with 40% mass fraction of hard segment possesses better mechanical properties.
  以HMDI、PTMG1000和MMT2為原料,硬段質(zhì)量分?jǐn)?shù)為40%25時(shí),所合成的納米蒙脫土-脂肪族聚氨酯彈性體具有較好的力學(xué)性能。
• The effects of hard segment content on the microstructure and viscosity of polyether PU and PUU were studied by FT-IR, DSC, viscosimeter.
  利用FT-IR,DSC,旋轉(zhuǎn)黏度計(jì)研究了硬段含量對(duì)聚醚型PU和PUU的微觀結(jié)構(gòu)及黏度的影響。
• It's caused by the micro phase separation degree of TPU is increased as well as the soft hard segment structure is perfected.
  研究認(rèn)為熱處理提高了TPU的微相分離程度,完善了TPU中的軟硬段結(jié)構(gòu)。
• For these PUU aqueous dispersions, the particle size decreases with the increase of the hard segment content, but their stability is enhanced.
  結(jié)果表明：隨硬段含量的增加，PUU水分散液的粒徑減小，穩(wěn)定性增加，室溫貯存期大于1年；
• Shape memory polyurethanes based on aliphatic diisocyanate HDI were synthesized with different hard segment contents to study the shape memory effect affected by hard segment.
  以脂肪族異氰酸酯HD I為硬段原料合成了脂肪族的形狀記憶聚氨酯,通過(guò)調(diào)節(jié)硬段含量研究了硬段結(jié)構(gòu)對(duì)形狀記憶性能的影響。
• When increasing hard segment content, the interaction between SPU moleculars is intensified whereas the miscibility of the blends in decreased consequently.
  多嵌段聚氨酯硬段含量的增加，加強(qiáng)了SPU分子間的相互作用，同時(shí)也減小了共混物兩組分的相容性。
返回 hard-segment